BGM24FR12A-Bromide series
PA6-(GF10+M20) FRProduct grade: Injection molding gradeProduct features: 10% glass fiber and 20% mineral-filled reinforced nylon 6, resistant to low-temperature impact, low warpage deformation
BGM24FR12A-Bromide series-Typical molding process
|
Dry |
Drum wind oven： 100～120℃，4～6h； Cycling warm air： 100～120℃，4～6h； Vacuum drying oven： 100～120℃，3～4h； |
|
Processing temperrature |
Feed section：225～240℃ Compressing section：235～260℃ Metering secion：240～260℃ |
|
Injection pressure |
70～130MPa |
|
Packing pressure |
40～90 MPa |
|
Mold temperature |
70～90℃ |
|
Back pressure |
8～15MPa |
BGM24FR12A
|
Test Item |
Test Standard |
Test Condition |
Unit |
Value |
|
Others |
||||
|
Product Identification |
ISO1043 |
—— |
—— |
PA6-(GF10+M20) FR |
|
Filler Content |
ISO3451-1 |
—— |
% |
30 |
|
Density |
ISO1183 |
23℃ |
g/cm³ |
1.52 |
|
Molding shrinkage(parallel/ normal) |
ISO 294-4 |
—— |
% |
0.3/0.8 |
|
Viscosity number |
ISO307 |
96%H2SO4,0.5g/dl |
ml/g |
130 |
|
Mechanical |
||||
|
Flexural Strength |
ISO178 |
23℃，2mm/min |
MPa |
85 |
|
Flexural Modulus |
ISO178 |
23℃，2mm/min |
MPa |
3800 |
|
Tensile Strength |
ISO527 |
Type I spline,50mm/min |
MPa |
50 |
|
Tensile Module |
ISO527 |
Type I spline,1mm/min |
MPa |
/ |
|
Tensile Strain at Break |
ISO527 |
Type I spline,50mm/min |
% |
2.8 |
|
Charpy Notched Impact Strength |
ISO179/1eA |
23℃ |
kJ/m2 |
12 |
|
Charpy Unnotched Impact Strength |
ISO179/1eU |
23℃ |
kJ/m2 |
40 |
|
Thermal |
||||
|
Melting Temperature |
ISO11357 |
—— |
℃ |
220 |
|
Heat Distortion Temperature |
ISO75-2 |
0.45MPa |
℃ |
/ |
|
1.8MPa |
℃ |
/ |
||
|
Electrical |
||||
|
CTI |
IEC60112 |
A |
V |
250 |
|
Volume Resistivity |
IEC60093 |
—— |
Ω•cm |
1014 |
|
Surface resistivity |
IEC60093 |
—— |
Ω |
1013 |
|
Flammability |
||||
|
Flammability |
UL-94 |
1.6mm |
Class |
V-0 |
|
GWFIT |
IEC60695 |
—— |
℃ |
/ |
All is typical data, only for reference, not the permit of quality assurance.